Study Some Properties for Manufactured Grinding Wheels by Use Different Abrasive Materials

    لتحميل الملف من هنا
Views  128
Rating  0
 مروة مرزة سلمان جرمط العجيلي 12/09/2019 06:30:07
تصفح هذه الورقة الالكترونية بتقنية Media To Flash Paper

This research includes study and manufacturing grinding wheels from different abrasive materials (silicon carbide (SiC) and alumina (Al2O3)) with particle size (154µm)) and glass binding material ( powder of window glass scrap with particle size (125µm)). The percentage of binding material was (8, 14, 20 % wt ). By using powder technology, samples of grinding wheels were produced from mixing the matrix and binding materials together and pressed at (110 MPa) by using steel alloy molds. After that, the samples were sintered at (700 ?C). The physical properties (density and porosity) and mechanical properties (hardness, bending strength, compressive strength and wear rate) were measured for all samples. The results showed that the higher hardness value was (517MPa) when silicon carbide was used with (20 % wt.) of glass binding material and lower wear rate was (0.088 g/cm2) when alumina was used with (20 % wt.) of glass binding material.

  • وصف الــ Tags لهذا الموضوع
  • silicon carbide, alumina, glass binding material, grinding wheels, wear rate.

هذه الفقرة تنقلك الى صفحات ذات علاقة بالمقالات الاكاديمية ومنها الاوراق البحثية المقدمة من قبل اساتذة جامعة بابل وكذلك مجموعة المجلات العلمية والانسانية في الجامعة وعدد من المدنات المرفوعة من قبل مشرف موقع الكلية وهي كالاتي:

قسم المعلومات

يمكنكم التواصل مع قسم معلومات الكلية في حالة تقديم اي شكاوى من خلال الكتابة الينا,يتوجب عليك اختيار نوع الرسالة التي تود ان ترسلها لادارة الموقع :