The technologically most important binary systems to achieve stabilization are based on the addition of various amounts of MgO, CaO, Y2O3 , CeO2 , and Sc2O3 to zirconia. The fact that the addition of small amounts of dopant oxides allows quenching of the cubic phase from high temperature directly to a metastable tetragonal phase, thus avoiding the deleterious monoclinic phase.
2.2.5.1 System ZrO2 – MgO
As shown in Figure 7.24, there is almost no solid solution of MgO in zirconia until the transformation temperature m ? t has been reached at 1240 °C. The solubility increases slowly with temperature, but beyond 1400 ° C a cubic solid solution with a eutectic composition of 87 mol% ZrO2+13mol% MgO becomes stable. Quenching of the material causes nucleation and the growth of oblate spheroidal precipitates of the tetragonal zirconia phase within the matrix of cubic zirconia (Figure 7.18). On further cooling below 1240 ° C the tetragonal particles transform to the monoclinic phase, causing transformation toughening (as described in detail above).
المادة المعروضة اعلاه هي مدخل الى المحاضرة المرفوعة بواسطة استاذ(ة) المادة . وقد تبدو لك غير متكاملة . حيث يضع استاذ المادة في بعض الاحيان فقط الجزء الاول من المحاضرة من اجل الاطلاع على ما ستقوم بتحميله لاحقا . في نظام التعليم الالكتروني نوفر هذه الخدمة لكي نبقيك على اطلاع حول محتوى الملف الذي ستقوم بتحميله .
الرجوع الى لوحة التحكم
|